Product Details

YX-133 High-Temperature Resistant Silicone-Based Resin

Keywords

Yanxun, silicon material, organic

Classification

Resin

Recommend

Message

Product Details

YX-133 Operating Instructions for High-Temperature-Resistant Silicon-Based Resin

1 Coating production: YX-133 Solvent-free, high-temperature-resistant polysilazane resin, when combined with high-temperature-resistant pigments and fillers such as alumina, boron nitride, and silicates, can be formulated into paints that are capable of withstanding high temperatures. 500-800 Flames at ℃ erode the surface (due to the relatively high brittleness of silicon-based resins, which makes them unsuitable for use as varnishes). When used in the laboratory, ... 500mL Solvent taken from the iron cup 50g The added pigment filler is 100 To 130g Add an appropriate amount of additive. 2 Millimeter-diameter zircon beads 100g , diameter 40mm PTFE grinding disc 3000-4000rpm Grinding 30-60 Minute slurry forming. 100-200 Filter the zirconia beads with a mesh, and store the slurry sealed for future use. Before spraying, 100 Add to the clay slurry 40 To 50 Ker YX-133 Stir well, 100 Filter the eyes for backup.

Spraying process	Operating Instructions	Note
Surface roughening	Before coating, sandblast or grind the substrate surface to remove rust, dust, dirt, and other contaminants adhering to the substrate surface—this is optimal. Sa2.5 , minimum St3 Grade without oxide scale ( GB/T 30790.4-2014 ).	This step can be skipped for clean substrates.
Surface cleaning	Use a dedicated cleaning agent or degreaser to remove any residual oil, grease, dust, and other contaminants from the brushed surface.	Affects adhesion, etc.
Substrate drying	Before coating, ensure that the substrate surface is dry and clean.	Affects adhesion, etc.
Coating preparation	Product mixing 3-5 Minutes, weigh according to construction requirements, 100 To 300 Filter the eyes for backup.
Coating application	For laboratory spraying use 1.0 The caliber spray gun boasts a superior appearance and better uniformity. After curing, the coating exhibits certain hydrophobic and oleophobic properties without compromising its ability to be repeatedly coated. The total film thickness measured should be below: 70 Trivial.	Use alkanes, lipids, ethers, and the like to clean the gun.
Solidification	Referring to the air spray coating data, the curing process is accompanied by solvent evaporation and produces a small amount of ammonia gas. Testing... Q235B Board 230 ℃保温 1h Can be cured; for complex substrates, increase the temperature or extend the curing time.	High-temperature testing should use temperature-resistant substrates.

2 Construction conditions: The substrate surface should be degreased. If sandblasting is not performed, loose debris or rust stains should be removed. Apply the coating at room temperature; dry film thickness: 25-50 Microns (add more for thicker coats) 500 Pigment below the eyes), curing temperature 190-230 ℃ and keep warm 20-40 minute 。