Product Details

YX-501 Operating Instructions for High-Temperature-Resistant Silicon-Based Resin

1 Coating production: YX-501 Made from high-temperature-resistant resins and additives, this paint—when formulated with high-temperature-resistant pigments such as alumina, boron nitride, and silicates—can withstand extremely high temperatures. 600-1100 Flame brushing at ℃ (due to the relatively high brittleness of silicon-based resins, they are not suitable for use as varnishes). When used in the laboratory, ... 500mL In an iron cup YX-501 Take 100g The added pigment filler is 100 To 130g , join 2 Millimeter-diameter zircon beads 120g , diameter 40mm PTFE grinding disc 3000-4000rpm Grinding 30-60 Minute paint formation. 100-200 Filter the zirconia beads and store them in a sealed container with paint for future use.

2 Construction conditions: The substrate surface should be degreased. If sandblasting is not performed, loose debris or rust stains should be removed. Apply the coating at room temperature; dry film thickness: 60-100 Microns (add more for thicker coats) 500 Pigment below the eyes), curing temperature 230-250 ℃ and keep warm 20-40 minute 。

Spraying process	Operating Instructions	Note
Surface roughening	Before coating, sandblast or grind the substrate surface to remove rust, dust, dirt, and other contaminants adhering to the substrate surface—this is optimal. Sa2.5 , minimum St3 Grade without oxide scale ( GB/T 30790.4-2014 ).	This step can be skipped for clean substrates.
Surface cleaning	Use a dedicated cleaning agent or degreaser to remove any residual oil, grease, dust, and other contaminants from the brushed surface.	Affects adhesion, etc.
Substrate drying	Before coating, ensure that the substrate surface is dry and clean.	Affects adhesion, etc.
Coating preparation	Product mixing 3-5 Minutes, weigh according to construction requirements, 120 To 300 Filter the eyes for backup.
Coating application	For laboratory spraying use 1.0 The caliber spray gun boasts a superior appearance and better uniformity. After curing, the coating exhibits certain hydrophobic and oleophobic properties without compromising its ability to be repeatedly coated. The total film thickness as tested should be below: 100 Trivial.	Use alkanes, lipids, ethers, and the like to clean the gun.
Solidification	Referring to the air spray coating data, the curing process is accompanied by solvent evaporation and produces a small amount of ammonia gas. Testing... Q235B Board 230 ℃保温 1h Can be cured; for complex substrates, increase the temperature or extend the curing time.	High-temperature testing should use temperature-resistant substrates.